Product Name: Thermoplastic Polyimide Resin

Item No.: SolverPI-Resin 6001

SolverPI-Resin 6001 is produced by SOLVER POLYIMIDE which has good machinability. It can be mould pressing,injection molding,extrusion molding.The themoplastic polymide can be reprocessed and mixed with graphite,carbon black,fiberglass,ceramic powder,carbon fiber,aramid fiber,metal powder,molybdenum disulfide,invisible material and so on to change its characters,producing the bearing,valve,seal part,pipe panel all kinds of mechine parts,and invisible marterial.

The characteristic of SolverPI-Resin 6001

·High heat resistence.Vissity temperature(Tf)264?,decomposition temperature=510?.

·Excellent lubricity.Low COFand low frictional loss.

·High insulation,low Coefficient of Linear Thermal Expansion,deformation resistence,acid and alkalicresistence,salt tolerance,non-corroding.

·Radiation resistant.N appearance change under the 200kGyirradiatiin of ray.

Extremely low hydroscopicity.Resistence to water wapor,no hydrolysis.

·Low thermalconductivity.Good thermal insulation properties,low calorific value when it runs up.

·The low dielectyic constant.High impedance,no reflection to radar,good base material of invisible material.

·Fire retardant level FV-level 0.

The applied range of SolverPI-Resin 6001

With the superior property,the ZTS-PI-I can be used in petrochemical industry,mining machinery,precision machinery,automobile industry,micro-electronic device,medical apparatus and instruments,aviation,aerospace,guided missile,naval vessels and so on.

In high speed and high pressure applications,parts with low COF and abrasion resistence.

Parts with good creep resistence and low plastic deformation.

Parts with good self-lubricating and good lubrication performance.

Parts with high bending?stretching?striking properties

Parts with high fire retardant level(no metal)

Parts with wave-transparent?microwave absorpting?invisible properties.

The permance index of SolverPI-Resin 6001

Terms of detection	Guideposts
Density(g/cm³)	1.25~1.35
Bending strength(MPa)(23?±2?)	?100
Flexural modulus(MPa)(23?±2?)	?3500
Impact strength Unnotched(KJ/?)(23?±2?)	?80
Impact strengrh notch(KJ/?)(23?±2?)	?6
Compressive strength(MPa)(23?±2?)	?50
Tensile strength(MPa)(23?±2?)	?75
Elongation%	3.0~8.0
Rockwell hardness(HRE)	40~60
Distortion temperature(18.6kg/?2)?	?200
Dilatation coefficient(23-200?),(10?5?/?/?)	3~8
Friction coefficient(PV=0.33MPa·m/s)	0.1~0.3
Wear volume(cm3)	?0.01
Dielectric constant(1KHz)	2.0~4.0
Surface resistance(O)	1010~1013
Volume resistance(O·m)	109~1012
Note:The standard is based on GB/T9352-2008«Plastic thermoplastic plastic material sample compaction».