Anticorrosive Powder Coating For Coal Mine Wells

Min Order

1
Product Unit

Pieces
Origin

China Mainland
Payment
Contact Now Start Order

Description

Product Detail

Advantages of XINKE Powder Coating:

1. Good adhesion between coating and substrate. Good mechanical ,heat-resistance and chemicals-resistance properties. It isn't easy to turn yellow and produce pinholes when baking. The film has fire-retardant property and extinguishing property to some extent.

2. Utilization rate can up to 8~10 m2/kg . Film thickness is 70µm (100% utilization rate). Practical coating zone varies with shapes of coating equipments and objects

3. Our raw material import from Holland and America,we can supply high qulity products to you.

4. Gloss and color of powder coating can be customized according to clients requirement .

5. We can also supply super weather-resistantance powder coating which can be guaranteed for 20~30 years.

Testing Report:

Main features	Good adhesive force, smooth coating and protection within large temperature range; Long-term anti-corrosive effect, compact, hard and durable coating, good impact resistance performance, flexibility and adhesion; Good anti-cathode disbanding capacity and good resistance to chemicals, solvent, water, sewage and sea water.
Application	It is applicable to the coating of crude oil pipelines, finished oil pipelines, oilfield water injection pipelines, sewage pipelines, inner wall of tap water pipelines, pipelines with flanges, elbows, valves, pumps and other deformed parts.
Product series	Powders in different colors can be made according to customers’ requirements.
Technical indexes	Appearance	Smooth surface, uniform gloss, no bubbles, cracks or shrinkage. Slight orange peel is allowed.
	Adhesive force (prying and stripping method)	1-3
	Bend resistance 4°	The coating is free from cracks (ambient temperature)
	Strength for impact resistance (J)	=11
	Abrasive resistance (1,000 h, 1,000 spins )mg	=20
	Film thickness µm	Common type: 350±50, the improved type: 500±50
	Cathodic disbanding (650O 48 h) mm	=8
	Salt spray test (1,000 h)	The film has no change.
	Volume resistivity O.M	=1×1,013
	Electrical strength mv/m =30	=30
	Curing condition	180O/10-15min 205O/8-10 min 230O/5-7 min