Anti Rust Paint

Min Order

1
Product Unit

Pieces
Origin

China Mainland
Payment
Contact Now Start Order

Description

Product Detail

725-H53-82 Fast drying micaceous iron oxide epoxy intermediate coating-Grey

Product Description

-A two pack abrasion resistant epoxy fast drying anticorrosive intermediate coating giving excellent long term anticorrosive protection.

-Suitable for application at low temperature

-VOC less than 260g/L

Intended Uses

-For use in atmospheric environment protection.

-For use at building, chemical plant, paper mill ,bridge approach, etc.

Product Information	Volume Solids	70%±2%
	Finish/Sheen	Gloss
	Typical Film Thickness	125 microns dry (187microns wet)
	Theoretical Coverage	5.3m²/L at typical film thickness
	Mix Ratio	4:1(volume)7.4:1(mass)
	Method of Application
	Airless Spray	Recommended
		Tip size range				0.38-0.53mm
		Output pressure				=17MPa
	Air Spray	Tip size range				2.0-3.0mm
		Output pressure				=0.4MPa
	Brush/Roller	For small area only
	Thinner	Not recommended. Use only in exceptional circumstances (volume 5%)
	Cleaner	HX-501
	Induction Period	Not necessary
	Drying Information
		-5?	5?		25?		35?
	Touch Dry	6h	2h		45min		30min
	Hard Dry	36h	24h		18h		12h
	Pot Life	6h	4h		2.5h		1.5h

	Overcoating Data Substrate Temperature
	Overcoated by	-5?	5?		25?		35?
		Min Max	Min Max		Min Max		Min Max
	725-H53-82	36h	24h		18h		12h
	725-J43-5	36h	24h		18h		12h
	725-BS43-91	72h	36h		20h		12h
	725-H42-30	36h	24h		18h		12h
	Storage	Store in cool and dry conditions. Well ventilate. Keep away from hot and fire. Shelf Life: 12 months minimum at 25?. Subject to re-inspection thereafter
	Pack Size	Part A		27.2kg/16L in 20 L container
		Part B		3.7kg/4L in 6L container
	?? Flash Point	Part A		Greater than 31?
		Part B		Greater than 28?
		Mixed paint		Greater than 31?
Surface Preparation	All surfaces to be coated should be clean, dry and free from contamination. Primed Surfaces The primer surface should be dry free from all contamination and 725-H53-82 must be applied within the overcoating intervals specified (consult the relevant product data sheet). Areas of breakdown, damage etc., should be prepared to the specified standard (e.gSa2½(GB/T 8923.1-2011)or Abrasive Blasting, or Power Tool Cleaning) and patch primed prior to the application of 725-H53-82. Metallic Zinc Primed Surfaces Ensure that surface of the primer is clean, dry and free from contamination and zinc salts before application of 725-H53-82. Ensure zinc primers are fully cured before overcoating. Repair The areas to be repaired should be cleaned to St3(GB/T 8923.1-2011)by mechanical method or higher level of surface prepared to Sa2.5(GB/T 8923.1-2011)by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.
Limitations	For maximum performance ambient curing temperature should be above 5?? In common with all epoxy base coatings, 725-H53-82 will exhibit chalking of the firm on UV exposure. Apply in good weather. Temperature of the surface to be coated must be least 3? above the dew point when the humidity is lower than 85%. The dry time and overcoating interval may change according to the environment factors. Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.
Duty statement	The data in the sheet base on the information from the laboratory and practice. The application may exceed the control, so we only ensure our product quality. We own the right of the data sheet modification without informing.