high grade P195GH P235GH P265GH S355J2H S335J0H low temperature Carbon Steel Pipe tube

  • Description
Product Detail

P195GH P235GH P265GH S355J2H S335J0H low temperature Carbon Steel Pipe tube 

????Description: Seamless steel tubes for pressure purposes.

Standard: EN10210-1, EN10216-2.

Applications: Used for piping in boilers.

Available steel grades: 195GH, P235GH, P265GH, S335J2H, S335J0H.

Specifications: O.D.: 6.0~1200mm; W.T.: 1~150mm; L: 5.8m; 11.8m; 12m or above. Modified specifications according to customer requirements.

Technology: Hot Rolled, Cold Drawn & Cold Rolled.

Chemical Composition and Mechanical Properties:

Standard

Grade

Chemical Composition

Mechanical Properties

C

Si

Mn

P=

S=

Cr=

Mo

(MPa)

(MPa)



L

t

EN10216-2

195GH

=0.13

=0.35

=0.70

0.025

0.02

0.3

=0.08

320~440

=195

=27

=25

P235GH

=0.16

=0.35

=1.20

0.025

0.02

0.3

=0.08

360~500

=235

=25

=23

P265GH

=0.20

=0.40

=1.40

0.025

0.02

0.3

=0.08

410~570

=265

=23

=21

Chemical Composition:

Steel grade

Type of deoxidationa

% by mass, maximum

C

Si

Mn

P

S

Nbc

Specified thickness (mm)

Steel name

Steel number

= 40

>40 =120

S235JRH

1.0039

FN

0,17

0,20

1,40

0,040

0,040

0,009

S275J0H

1.0149

FN

0,20

0,22

1,50

0,035

0,035

0,009

S275J2H

1.0138

FF

0,20

0,22

1,50

0,030

0,030

S355J0H

1.0547

FN

0,22

0,22

0,55

1,60

0,035

0,035

0,009

S355J2H

1.0576

FF

0,22

0,22

0,55

1,60

0,030

0,030

S355K2H

1.0512

FF

0,22

0,22

0,55

1,60

0,030

0,030

a. The deoxidation methods are designated as follows:

FN = Rimming steel not permitted

FF = Fully killed steel containing nitrogen binding elements in amounts sufficient to bind

available nitrogen

(e.g. min. 0,020 % total Al, or  0,015 % soluble Al).

b. It is permissible to exceed the specified values provided that for each increase of 0,001 % N the P max.  content is also reduced by 0,005 %. The N content of the  cast analysis, however, shall not be more than 0,012 %.

c. The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content  of 0,020 % with a minimum Al/N ratio of 2:1, or if sufficient  other N-binding elements are present. The N-binding elements shall be  recorded in the Inspection Document.

Mechanical Properties:

Steel grade

Minimum yield strength ReH

Tensile strength Rm

Minimum elongation A a b

Minimum impact energy KV d



MPa

MPa

%

J

steel name

steel number

Specified thickness

Specified thickness

Specified thickness

Specified thickness

mm

mm

mm

mm

= 16

= 16

> 40

> 63

> 80

> 100

= 3

> 3

> 100

= 40

> 40

> 63

> 100

-20°C

0°C

20°C

= 40

=63

= 80

= 100

= 120

= 100

= 120

=63

= 100

= 120

S235JRH

1.0039

235

225

215

215

215

195

360-510

360-510

350-500

26

25

24

22

/

/

27

S275J0H

1.0149

275

265

255

245

235

225

430-580

410-560

400-540

23

22

21

19

/

27

/

S275J2H

1.0138

27

/

/

S355J0H

1.0547

355

345

335

325

315

295

510-680

470-630

450-600

22

21

20

18

/

27

/

S355J2H

1.0576

27

/

/

S355K2H

1.0512

40 e

/

/

a Longitudinal values. Transverse  values are 2 % lower.

b For thicknesses < 3 mm, see  9.2.2.

c The impact properties are  verified only when Option 1.3 is specified.

d For impact properties for  reduced section test pieces see 6.6.2.

e This value corresponds to 27J at  –30 °C (see EN 1993-1-1).

Send your message to this supplier
To:  

Jiangsu Jinguan Special Steel Pipe Co.Ltd

* Content:  

For better quotations, include:

- A self introduction

- Special requests, if any

Quantity:  
  
You May Like
Not exactly what you want? One request, multiple quotations Get Quotations Now >>
China Mainland Favorites
Transaction Level:

* Quantity: